U1_t glass chemistry
Click here to access sample quantification.
| SAMPLE |
SiO2 |
TiO2 |
FeO |
MgO |
CaO |
Al2O3 |
Na2O |
BaO |
Cl |
P2O5 |
K2O |
Total-Wt% |
| U1_t_77_glass |
65.557 |
0.411 |
2.147 |
0.326 |
1.051 |
16.519 |
5.555 |
0.058 |
0.564 |
0.127 |
5.584 |
97.898 |
| U1_t_77_glass |
68.355 |
0.536 |
2.523 |
0.255 |
0.506 |
14.326 |
5.254 |
0 |
0.707 |
0.037 |
5.462 |
97.96 |
| U1_t_77_glass |
66.3 |
0.405 |
2.179 |
0.301 |
0.828 |
16.725 |
6.095 |
0 |
0.594 |
0.042 |
5.513 |
98.983 |
| U1_t_77_glass |
66.566 |
0.417 |
2.2 |
0.28 |
0.887 |
16.973 |
6.166 |
0.047 |
0.579 |
0.074 |
5.354 |
99.541 |
| U1_t_77_glass |
65.195 |
0.492 |
2.236 |
0.302 |
0.84 |
16.377 |
5.806 |
0.049 |
0.593 |
0.082 |
5.328 |
97.299 |
| Average |
66.394 |
0.452 |
2.257 |
0.292 |
0.822 |
16.184 |
5.775 |
0.031 |
0.607 |
0.072 |
5.448 |
98.336 |
| St Deviation |
1.227 |
0.059 |
0.152 |
0.027 |
0.198 |
1.063 |
0.38 |
0.028 |
0.057 |
0.036 |
0.107 |
0.905 |
| U1_t_77_plagio |
63.962 |
0.13 |
0.578 |
0.014 |
3.088 |
22.236 |
8.095 |
0.44 |
0.019 |
0 |
2.461 |
101.023 |
| U1_t_77_plagio |
66.252 |
0.194 |
1.069 |
0.09 |
1.475 |
19.402 |
7.213 |
0.163 |
0.166 |
0.035 |
4.26 |
100.317 |
| U1_t_77_plagio |
62.435 |
0.1 |
0.537 |
0.016 |
4.339 |
23.503 |
7.777 |
0.422 |
0.017 |
0.007 |
1.458 |
100.611 |
| U1_t_77_plagio |
62.228 |
0.08 |
0.498 |
0.003 |
4.128 |
23.326 |
7.869 |
0.564 |
0.005 |
0 |
1.632 |
100.332 |
| Average |
63.719 |
0.126 |
0.67 |
0.031 |
3.258 |
22.117 |
7.738 |
0.397 |
0.052 |
0.01 |
2.453 |
100.571 |
| St Deviation |
1.857 |
0.05 |
0.268 |
0.04 |
1.308 |
1.895 |
0.375 |
0.168 |
0.077 |
0.016 |
1.282 |
0.33 |
|